Aluminum
Below is a list of Aluminum
//High strength in elevated temperatures.
EOS Aluminium Al2139 AM is a 2000-series high strength alloy specifically designed for AM. It demonstrates outstanding performance in elevated temperatures up to 200 °C. The fast and simple heat treatment procedure enables an affordable part production.
Typical Part Properties (T4 heat treated state):
- Chemical composition modified from Aluminium Association Teal Sheet for Al2139
- Ultimate Tensile Strength: 520 MPa
- Yield Strength: 460 MPa
- Elongation @ Break: 4%
EOS Aluminium Al2139 AM System Compatibility:
Download Spec Sheet//Heat-treatable with high strength & high elongation.
EOS Aluminum Al5X1 is a heat-treatable aluminum alloy designed for AM to offer a compelling combination of high strength and high elongation. The recommended single-step heat treatment does not require a water quench and enables robust part production.
Typical Part Properties:
- Chemical composition in compliance with: Designed for AM
- Ultimate Tensile Strength: 410 MPa
- Yield Strength: 380 MPa
- Elongation @ Break: 14%
EOS Aluminum Al5X1 System Compatibility:
Download Spec Sheet//Light weight & corrosion resistance.
Parts printed using EOS Aluminum AlF357 offer a combination of low weight, corrosion resistance and high dynamic load bearing capacity.
Typical Part Properties:
- Chemical composition in compliance with AlSi7Mg0.6, SAE AMS 4289
- Ultimate Tensile Strength: 330 MPa
- Yield Strength: 260 MPa
- Elongation @ Break: 11%
EOS Aluminum AlF357 System Compatibility:
Download Spec Sheet//Good strength and dynamic load bearing capacity.
Parts printed using EOS Aluminum AlSi10Mg offer good strength, hardness and dynamic properties as well as good thermal properties and low weight.
Typical Part Properties:
- Chemical composition in compliance with AlSi10Mg
- Ultimate Tensile Strength: 460 MPa
- Yield Strength: 245 MPa
- Elongation @ Break: 5%
EOS Aluminum AlSi10Mg System Compatibility:
Download Spec Sheet